蔡秀丽,吕建平,刘姣姣,张俊贺,王方银.双层包覆香精微胶囊的制备及性能研究[J].包装工程,2013,34(11):31-34.
CAI Xiu-li,LYU Jian-ping,LIU Jiao-jiao,ZHANG He-jun,WANG Fang-yin.Preparation and Property of Double-layered Microencapsulated Fragrance[J].Packaging Engineering,2013,34(11):31-34.
双层包覆香精微胶囊的制备及性能研究
Preparation and Property of Double-layered Microencapsulated Fragrance
投稿时间:2013-04-08  修订日期:2013-06-10
DOI:
中文关键词: 双层包覆  香精  热稳定性  缓释性能
英文关键词: double-layered capsulation  perfume  thermal stability  sustained-release
基金项目:广东省部产学研项目(2010B0090400014)
作者单位
蔡秀丽 合肥工业大学, 合肥 230009 
吕建平 合肥工业大学, 合肥 230009 
刘姣姣 合肥工业大学, 合肥 230009 
张俊贺 合肥工业大学, 合肥 230009 
王方银 安徽美佳新材料股份有限公司, 芜湖 241200 
摘要点击次数:
全文下载次数:
中文摘要:
      以密胺树脂和丙烯酸酯为囊材,采用微胶囊双层包覆方法改善茉莉香精的耐热和缓释性能,采用傅里叶红外光谱仪(FT-IR)和扫描电镜(SEM)对微胶囊的结构和形貌进行了表征,结果表明包覆完全,形貌规整。 热重法 TG 测得单层微胶囊在 200 ℃以下时匀速失重,在 200 ~ 250 ℃快速失重,而双层微胶囊的失重速率明显小于单层微胶囊。 50 ℃恒温热失重法测得双层微胶囊的释放速率小于单层微胶囊,27 d 后的失重率小于 10. 1% 。
英文摘要:
      Microencapsulated jasmine perfume was prepared by double-layered capsulation method to improve its thermal stability and sustained-release, in which melamine-formaldehyde and acrylic ester were chose as wall materials. The obtained microcapsules were characterized in terms of morphology and chemical structure by scanning electron microscopy ( SEM), Fourier infrared spectrometer ( FT-IR) and scanning electron microscopy ( SEM), and results showed that the oil-soluble fragrance had been encapsulated completely. Furthermore, weight loss rate of capsulated jasmine perfume was also measured by thermo-gravimetry analysis. It was found that in case of single-layered microcapsule, the weight loss was kept in constant before 200 ℃ , and then accelerated rapidly from 200 ℃ to 250 ℃ . The weight loss rates of double-layered microcapsules, on the other hand, were much lower than those of single-layered ones. Thermostat thermal weight loss in 50 ℃ showed that the perfume release rate of double-layered microcapsule was significantly lower than that of single-layered one, and the weight loss rate was less than 10. 1% after 27 days.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第22593661位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号