于振菲,吴佳鑫,赵子龙,王爽爽,靳烨,董同力嘎.聚乳酸单轴拉伸膜的包装特性研究[J].包装工程,2014,35(1):23-27,33.
YU Zhen-fei,WU Jia-xin,ZHAO Zi-long,WANG Shuang-shuang,JIN Ye,DONG Tungalag.Packaging Characteristics of Uniaxially Stretched Poly( L-lactic acid) Film[J].Packaging Engineering,2014,35(1):23-27,33.
聚乳酸单轴拉伸膜的包装特性研究
Packaging Characteristics of Uniaxially Stretched Poly( L-lactic acid) Film
投稿时间:2013-04-15  修订日期:2013-12-01
DOI:
中文关键词: 聚乳酸  阻隔性能  结晶性能  热收缩性能
英文关键词: poly( L-lactic acid)  crystallization behavior  barrier property  thermal shrinking
基金项目:国家自然科学基金(51163010) ;内蒙古草原英才科研基金(2011)
作者单位
于振菲 内蒙古农业大学, 呼和浩特 010018 
吴佳鑫 内蒙古农业大学, 呼和浩特 010018 
赵子龙 内蒙古农业大学, 呼和浩特 010018 
王爽爽 内蒙古农业大学, 呼和浩特 010018 
靳烨 内蒙古农业大学, 呼和浩特 010018 
董同力嘎 内蒙古农业大学, 呼和浩特 010018 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究了不同拉伸比的 PLLA 薄膜的热学性能、阻隔性能和热收缩性能。 方法 采用双螺杆挤流延试验机单轴拉伸制备了不同拉伸比的 PLLA 热收缩膜和定向拉伸膜,采用差示扫描量热分析仪( DSC) 、透湿仪和透氧仪对不同拉伸比的 PLLA 薄膜的热学性能和阻隔性能进行了评估,并对 PLLA膜的热收缩性进行了测定。 结果 热收缩膜的拉伸比由 1 增大到 6 . 5 时,PLLA 的结晶度由 0 . 2% 增加到 41 . 8% ,结晶速率明显提高,阻隔性得到了一定的改善。 随着拉伸比例的增大,热收缩率随之增大。 定向拉伸膜的结晶度得到了大幅度提高,其阻隔性也得到了改善,但不呈现热收缩性。 结论 通过单轴拉伸可以有效地提高 PLLA 薄膜的结晶速率和结晶度,经过中等拉伸比例的 PLLA 薄膜,其阻湿阻氧能力相对较强。
英文摘要:
      Objective To study the thermal, barrier and thermal shrinkage properties of PLLA films with different draw ratios. Methods PLLA thermal shrinkage films with different draw ratios and uniaxially stretched PLLA films were prepared by a twin-screw extruder. Thermal shrinkage and barrier properties of the PLLA films with different draw ratios were measured by an DSC, a water vapor permeability tester and an oxygen permeability tester. Results The crystallinity of PLLA increased from 0. 2% at ratio = 1 to 41. 8% at ratio = 6. 5, and the crystallization rate and crystallinity increased significantly. The barrier properties of PLLA were improved by the orientation and crystallization. The shrinkage films showed an excellent thermal shrinkage behavior, while the stretched films losted their thermal shrinkage. Conclusion Uniaxial stretching could effectively improve the crystallization rate and crystallinity of PLLA films. The moisture and oxygen barrier properties of the PLLA films are relatively good after medium stretching.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第21112876位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号