刘洋,莫灿梁,张新昌.微波工艺用于过氧化氢漂白 OCC纸浆研究[J].包装工程,2014,35(11):59-62,75.
LIU Yang,MO Can-liang,ZHANG Xin-chang.Hydrogen Peroxide Bleaching of OCC Pulp with Microwave Technology[J].Packaging Engineering,2014,35(11):59-62,75.
微波工艺用于过氧化氢漂白 OCC纸浆研究
Hydrogen Peroxide Bleaching of OCC Pulp with Microwave Technology
投稿时间:2014-02-14  修订日期:2014-06-01
DOI:
中文关键词: OCC纸浆  微波工艺  漂白  过氧化氢
英文关键词: OCC pulp  microwave heating  bleaching  hydrogen peroxide
基金项目:
作者单位
刘洋 江南大学 无锡 214122 
莫灿梁 东莞市汇林包装有限公司 东莞 523520 
张新昌 东莞市汇林包装有限公司 东莞 523520 
摘要点击次数:
全文下载次数:
中文摘要:
      目 的 研究微波工艺代替水浴加热对过氧化氢漂白 OCC 纸浆漂白效果的影响。 方法 OCC 纸浆经 EDTA 处理后加入硫酸镁、硅酸钠和氢氧化钠搅拌均匀 , 在 60 ℃水浴中加热 3 min, 在微波工艺下进行双氧水漂白 , 研究了碱比(m(NaOH)∶m(H2O2))、H2O2用量、微波功率和微波时间对纸浆亮度(CIE L*)和残液COD 值的影响, 并与常规水浴加热漂白进行了对比。 结果 当碱比为 0.2、H2O2的质量分数为 2%、微波功率为 300 W、微波时间为 150 s 时, 纸浆亮度提高了 69.3%, 与水浴加热漂白相比提高了 25.51%, COD 值降低了 32.43%。 结论 微波工艺可以明显缩短OCC 纸浆漂白的时间, 提高漂白效率,获得比水浴加热漂白更高的纸浆亮度,残液COD 值也处于更低水平。
英文摘要:
      Objective To study the effect of microwave technology on OCC pulp bleaching with hydrogen peroxide. Methods OCC pulp was first treated by EDTA, and then evenly mixed with magnesium sulfate, sodium silicate and sodium hydroxide. The pulp was heated in a 60℃ water bath for 3 minutes, and then heated in a microwave during the hydrogen peroxide bleaching. The influences of alkali ratio (m(NaOH) ∶ m(H2O2)), H2O2 dosage, microwave power and heating time on the pulp brightness(CIE L*) and the COD of raffinate were studied, and compared to those of bleaching with conventional water bath heating. Results When the alkali ratio was 0.2, the H2O2 dosage was 2%, the microwave power was 300 W, the heating time was 150 s, the pulp brightness was increased by 69.3%. Compared to the water bath heating, the pulp brightness was increased by 25.51%, and the numerical value of COD was decreased by 32.43%. Conclusion Microwave technology could not only significantly shorten the bleaching time, improve the bleaching efficiency, but also achieve higher pulp brightness and lower numerical value of COD than bleaching with water bath heating.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第21018543位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号