文章摘要
赖惟永,侯伦灯,叶博雄,于再君,苏团.迷彩刨花板的研制及力学性能分析[J].包装工程,2016,37(13):38-42.
LAI Wei-yong,HOU Lun-deng,YE Bo-xiong,YU Zai-jun,SU Tuan.Development of Camouflage Particle Board and Analysis of Its Mechanical Properties[J].Packaging Engineering,2016,37(13):38-42.
迷彩刨花板的研制及力学性能分析
Development of Camouflage Particle Board and Analysis of Its Mechanical Properties
投稿时间:2016-04-23  修订日期:2016-07-10
DOI:
中文关键词: 迷彩刨花板  迷彩配色方案  染色大片刨花  相对自由基浓度  力学性能
英文关键词: camouflage particle board  camouflage color scheme  dyeing flake board  relative free radicals concentration  mechanical property
基金项目:福建省教育厅 B 类项目(JB10169)
作者单位
赖惟永 龙岩学院龙岩 364012 
侯伦灯 福建农林大学福州 350002 
叶博雄 国立云林科技大学台湾 云林 64001 
于再君 龙岩学院龙岩 364012 
苏团 龙岩学院龙岩 364012 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究不同色彩处理方式对大片刨花表面相对自由基浓度的影响,及不同迷彩组合色对板材力学性能的影响。 方法 通过对大片刨花进行煮沸染色,采用电子自旋共振波谱仪对各类处理方式刨花检测其相对自由基浓度,然后根据不同迷彩色方案进行压制板材,采用万能力学电子实验仪检测其力学性能,分析不同迷彩刨花板的相对自由基浓度与力学性能的关系。 结果 刨花的不同处理方式(煮沸与否、染色与否、染料种类、染料浓度等)对其相对自由基浓度影响方差分析 F值为 119.4; 5 类不同色刨花板的力学性能 MOR 方差值为 9.38;丛林迷彩板材力学强度最高,弹性模量为 5883.47 MPa,结合强度为 0.68 MPa,静曲强度为 52.37 MPa。 结论 各迷彩色酸性染料染色处理对刨花表面的相对自由基浓度有显著影响,有益于板材的胶合性能;4 种常见迷彩配色方案中,板材的力学性能也有所提升,尤其是丛林迷彩板材具备较优的力学性能。
英文摘要:
      This work aimed to study the effects of different color treatments on the relative free radicals concentration of boiling dyeing flake surface, and the effects of different camouflage color combinations on the mechanical properties of the board. During the boiling dyeing of flakes, the relative free radicals of flakes which were differently treated were detected by the electron spin resonance spectrometer. Then different plates were pressed by different camouflage color schemes. Their mechanical properties were detected by universal mechanical electronic experiment instrument. And the relationship between the relative free radicals concentration and the mechanical properties of different Camouflage Particle boards was analyzed in this paper. The F value of variance of different treatments (boiled or not, dyed or not, the type of dye, the concentration of dye, etc.) was 119.4. The MOR variance of the mechanical properties of five different Camouflage Particle boards was 9.38. Jungle camouflage plates had the best mechanical properties, with parameters of MOE(5883.47 MPa), IB(0.68 MPa), MOR(52.37 MPa). Different dyeing treatments of acid dyes had significant influence on the relative free radicals concentration, and they were beneficial to the bonding strength of plate. The mechanical properties of plate were also improved by the four common camouflage color schemes. Especially, jungle camouflage plates had relatively good mechanical properties.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20794285位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号