文章摘要
贝荣华,黄崇杏,陈强,李志嘉,苏红霞,王健.SiOx/PET复合薄膜的力学性能及阻隔性能[J].包装工程,2017,38(19):57-62.
BEI Rong-hua,HUANG Chong-xing,CHEN Qiang,LI Zhi-jia,SU Hong-xia,WANG Jian.Mechanical Properties and Barrier Properties of SiOx/PET Composite Films[J].Packaging Engineering,2017,38(19):57-62.
SiOx/PET复合薄膜的力学性能及阻隔性能
Mechanical Properties and Barrier Properties of SiOx/PET Composite Films
投稿时间:2016-12-27  修订日期:2017-10-10
DOI:
中文关键词: SiOx层  结构成分  力学性能  阻隔性能
英文关键词: SiOx layer  structural composition  mechanical properties  barrier properties
基金项目:国家自然科学基金(2156070033);广西自然科学基金(2015jjAA60108)
作者单位
贝荣华 广西大学南宁 530004 
黄崇杏 广西大学南宁 530004 
陈强 北京印刷学院北京 102600 
李志嘉 广西大学南宁 530004 
苏红霞 广西大学南宁 530004 
王健 广西大学南宁 530004 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 基于氧化硅(SiOx)镀层优异的性能,研究不同厚度的SiOx层对SiOx/PET复合薄膜力学性能和阻隔性能的影响,以期得到性能较优的SiOx/PET复合薄膜。方法 以自制的聚对苯二甲酸乙二醇酯(PET)薄膜为基材,采用等离子体增强化学气相沉积法沉积得到SiOx层厚度分别为40,150,230,320 nm的SiOx/PET复合薄膜,并进行傅里叶变换红外线光谱分析、力学性能和阻隔性能测试,以及薄膜表观形貌分析。结果 沉积SiOx层后,SiOx/PET复合薄膜拉伸强度和断裂伸长率随SiOx层厚度的增大先增大后减小,氧气透过率和水蒸气透过率则出现明显衰减而后逐渐平缓的趋势。SiOx层厚度达150~230 nm时,复合薄膜的力学性能和阻隔性能表现较优,拉伸强度、断裂伸长率、氧气透过率以及水蒸气透过率分别提高了约25.0%,20.9%,79.3%,77.3%。结论 适宜厚度的SiOx层可以使得SiOx/PET复合薄膜同时具备较优的力学性能和阻隔性能。
英文摘要:
      The work aims to obtain the SiOx/PET composite film with better performance by studying the effects of SiOx layer of different thicknesses on the mechanical properties and the barrier properties of SiOx/PET composite films, based on the excellent properties of silicon oxide (SiOx) layer. The SiOx layers with thickness of 40, 150, 230 and 320 nm were obtained by plasma enhanced chemical vapor deposition, with the self-made polythylene terephthalate (PET) film as the base material. Then, the Fourier transform infrared spectroscopy, and tests of mechanical properties and barrier properties were carried out, and the apparent morphology of the film was analyzed. After the SiOx layer was deposited, the tensile strength and elongation at break of the SiOx/PET composite films were increased first and then decreased with the increase in the thickness of SiOx layer, and the oxygen permeability and water vapor transmission rate were significantly attenuated and then gradually became gentle. The mechanical properties and barrier properties of the composite film were better when the thickness of SiOx layer was in the range of 150~230 nm. The tensile strength, elongation at break, oxygen permeability and water vapor transmission rate were improved by about 25.0%, 20.9%, 79.3% and 77.3%, respectively. The SiOx layer with suitable thickness can provide the SiOx/PET composite film with better mechanical properties and the barrier properties.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第22553034位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号