王睿娜,韩磊,惠非琼,陈友林.镀陶烟用内衬纸防潮保润保香性研究[J].包装工程,2019,40(15):130-135.
WANG Rui-na,HAN Lei,HUI Fei-qiong,CHEN You-lin.Moisture Proofing, Moisture Retention and Fragrance Retention of Ceramic-plated Cigarette Lining Paper[J].Packaging Engineering,2019,40(15):130-135. |
| 镀陶烟用内衬纸防潮保润保香性研究 |
| Moisture Proofing, Moisture Retention and Fragrance Retention of Ceramic-plated Cigarette Lining Paper |
| 投稿时间：2019-02-27 修订日期：2019-08-10 |
| DOI：10.19554/j.cnki.1001-3563.2019.15.021 |
| 中文关键词: 烟用内衬纸 镀陶 防潮 保香 保润 |
| 英文关键词: cigarette lining paper ceramic-plated moisture proofing fragrance retention moisture retentio |
| 基金项目:贵州中烟工业有限责任公司科技创新（黔烟工技〔2017〕53号）（GZZY/KJ/JS/2017CN003-0） |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究对比陶制直镀内衬纸与常规直镀内衬纸的防潮保润保香性能。方法 对镀陶和常规直镀内衬纸进行SEM，BET和透湿率及透氧率检测，并将2种内衬纸卷制的成品卷烟放置于高温高湿、干燥、常温常湿等条件下平衡85 d，随后对拆包不同时长的卷烟进行烟支含水率检测，同时采用静态顶空气相色谱-质谱联用仪测定卷烟滤棒及烟丝中香精的主要成分含量。结果 与常规直镀内衬纸相比，镀陶直镀内衬纸的表面致密性和比表面积明显较优，且其氧气透过率略小，水蒸气透过率较小。在高温高湿和干燥条件下，镀陶样品的烟支含水率与初始设计值较为接近；在常温常湿条件下，2种内衬纸包装的烟支含水率虽在拆包前30 h无明显区别，但在35 h后，常规直镀内衬纸包装的烟支含水率显著下降，不满足设计要求。结论 镀陶直镀内衬纸的防潮效果较好、保香效果较好、保润效果略好。镀陶烟用内衬纸的工艺还有待进一步调整，以进一步提高其防潮保香保香效果。 |
| 英文摘要: |
| The work aims to investigate and compare the moisture proofing, moisture retention and fragrance retention of ceramic direct-plated lining paper and conventional direct-plated lining paper. SEM, BET, moisture permeability and oxygen permeability tests were carried out to detect the ceramic-plated lining paper and conventional direct-plated lining paper. These finished cigarettes made of these two kinds of lining paper were placed under three conditions, including high temperature and high humidity environment, dry conditions and normal temperature and humidity conditions for 85 days. After that, the moisture contents of these cigarettes subject to different unpacking time were tested. At the same time, static headspace GC-MS was used to determine the main components of the tobacco essence in the cigarette filter rod and cut tobacco. Compared with the conventional direct-plated lining paper, the surface compactness and specific surface area of ceramic direct-plated lining paper were better, and its oxygen permeability was slightly low, and its water vapor permeability was lower. Under high temperature, high humidity and dry conditions, the cigarette moisture content of the samples packaged in ceramic-plated lining paper was close to the original design value. At room temperature and humidity, the moisture contents of cigarettes in two kinds of lining paper packaging were of no significant difference in 30 h before unpacking. However, 35 h later, the moisture content of cigarettes packaged with conventional direct-plated lining paper decreased significantly. It didn't meet the requirements of design value. The direct-plated lining paper has better effects on moisture proofing, fragrance retention and moisture retention.The technology of ceramic-plated cigarette lining paper still needs to be adjusted to improve its effect on moisture proofing, moisture retention and fragrance retention. |
|