苏亚男,经德齐,张兴华,张寿春.磺化聚醚醚酮上浆剂的制备及其对碳纤维性能的影响[J].包装工程,2020,41(21):45-53.
SU Ya-nan,JING De-qi,ZHANG Xing-hua,ZHANG Shou-chun.Preparation of Sulfonated Poly (Ether Ether Ketone) Sizing Agent and Its Effect on the Properties of Carbon Fiber[J].Packaging Engineering,2020,41(21):45-53.
磺化聚醚醚酮上浆剂的制备及其对碳纤维性能的影响
Preparation of Sulfonated Poly (Ether Ether Ketone) Sizing Agent and Its Effect on the Properties of Carbon Fiber
投稿时间:2020-04-07  
DOI:10.19554/j.cnki.1001-3563.2020.21.0007
中文关键词: 碳纤维  磺化聚醚醚酮上浆剂  表面性能  单丝拉伸强度
英文关键词: carbon fiber  SPEEK sizing agent  surface properties  singles fiber tensile strength
基金项目:中科院青年创新促进会项目(2012140);中国科学院战略性先导科技专项(A类)(XDA17040519);山西省重点研发计划(201803D121042)
作者单位
苏亚男 中国科学院山西煤炭化学研究所 碳纤维制备技术国家工程实验室太原 030001
中国科学院大学 材料与光电研究中心北京 100049
中国科学院山西煤炭化学研究所 中国科学院炭材料重点实验室太原 030001 
经德齐 中国科学院山西煤炭化学研究所 碳纤维制备技术国家工程实验室太原 030001
中国科学院山西煤炭化学研究所 中国科学院炭材料重点实验室太原 030001 
张兴华 中国科学院山西煤炭化学研究所 碳纤维制备技术国家工程实验室太原 030001
中国科学院山西煤炭化学研究所 中国科学院炭材料重点实验室太原 030001 
张寿春 中国科学院山西煤炭化学研究所 碳纤维制备技术国家工程实验室太原 030001
中国科学院大学 材料与光电研究中心北京 100049
中国科学院山西煤炭化学研究所 中国科学院炭材料重点实验室太原 030001 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 制备一种热塑性上浆剂,以期改善碳纤维的表面性能以及单丝拉伸性能。方法 通过直接磺化法制备磺化聚醚醚酮水性上浆剂,并通过喷涂法对未上浆的T300碳纤维进行上浆处理,研究制得上浆剂的结构特征、性能以及其对碳纤维性能的影响。结果 制得磺化聚醚醚酮的磺化度约为74%,以此为主浆料配制的水性上浆剂具有良好的成膜性和储存稳定性。经上浆处理后,碳纤维表面形成了连续的磺化聚醚醚酮上浆层,表面官能团含量明显增加,树脂微滴在纤维表面的接触角降低。此外,上浆层可以弥补纤维表面的部分缺陷,使得上浆后碳纤维的单丝拉伸强度提高了5%。结论 磺化聚醚醚酮上浆剂可以有效改善碳纤维的表面性能及单丝拉伸性能。
英文摘要:
      The work aims to prepare a thermoplastic sizing agent to improve the surface properties and monofilament tensile properties of CF.The sulfonated poly (ether ether ketone) (SPEEK) sizing agent was prepared by a simple sulfonation process, and was applied to size the unsized T300 carbon fiber (CF) by spraying. The structural performance and properties of the sizing agent and its effect on the properties of CF were studied. The results demonstrated that the degree of sulfonation of SPEEK was about 74%. The water borne sizing agent prepared with it as the main slurry had good film-forming property and storage stability. After sizing treatment, a continuous SPEEK sizing layer was formed on the surface of CF. Also, the surface functional groups of SPEEK sized CF increased significantly, and the contact angle of resin droplets on the surface of fiber decreased. Besides, the sizing layer can heal some defects of the CF surface. Thus, compared with unsized CF, the tensile strength of SPEEK sized CF was increased by 5%. Therefore, the SPEEK sizing treatment can improve the surface properties and monofilament tensile properties of CF.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第21104002位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号