谢利,陈美,刘晓慧,徐玥阳,李德祥,孙乐天,张璇,周星.废弃PET资源化低聚物多元醇制备聚氨酯胶黏剂性能研究[J].包装工程,2024,45(11):1-12.
XIE Li,CHEN Mei,LIU Xiaohui,XU Yueyang,LI Dexiang,SUN Letian,ZHANG Xuan,ZHOU Xing.Properties of Polyurethane Adhesive Prepared From Waste PET Resource Oligomer Polyol[J].Packaging Engineering,2024,45(11):1-12.
废弃PET资源化低聚物多元醇制备聚氨酯胶黏剂性能研究
Properties of Polyurethane Adhesive Prepared From Waste PET Resource Oligomer Polyol
投稿时间:2024-03-14  
DOI:10.19554/j.cnki.1001-3563.2024.11.001
中文关键词: 废弃PET  聚氨酯  胶黏剂
英文关键词: waste PET  polyurethane  adhesive
基金项目:国家自然基金委面上项目(52372093);中国博士后科学基金(2019M663785);陕西省重点研发项目(2023GXLH-045);西安市碑林区应用技术研发类项目(GX2247;GX2232);国家级大学生创新创业训练计划项目(202310700050)。
作者单位
谢利 西安理工大学 印刷包装与数字媒体学院西安 710048 
陈美 西安理工大学 印刷包装与数字媒体学院西安 710048 
刘晓慧 西安理工大学 印刷包装与数字媒体学院西安 710048 
徐玥阳 西安理工大学 印刷包装与数字媒体学院西安 710048 
李德祥 西安理工大学 印刷包装与数字媒体学院西安 710048 
孙乐天 西安理工大学 印刷包装与数字媒体学院西安 710048 
张璇 西安理工大学 印刷包装与数字媒体学院西安 710048 
周星 西安理工大学 印刷包装与数字媒体学院西安 710048 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 采用预处理后的废弃PET降解产物作为扩链剂,制备不释放甲醛、附着力强、耐久性好、具有一定力学性能的胶黏剂,以替代传统甲醛基胶黏剂。方法 将废弃PET降解得到的低聚物多元醇进行洗脱预处理,再与异氰酸酯通过逐步聚合反应制得新型聚氨酯胶黏剂(PUa)。结果 在低温/室温环境下,PUa对纸张、玻璃、木材等基材的黏附强度超过126 kPa;经过黏附-解黏附-黏附38次循环黏结后,仍保留至少39.2%的黏附性,具有优良的重复黏结性能。结论 利用废弃PET制备的新型聚氨酯胶黏剂的热稳定性和黏结性能较好,环境适应性好,在轻质缓冲包装领域具有巨大的潜在应用价值。该研究可为塑料废弃物资源化利用提供高附加值的解决方案,还可以为缓解石油资源短缺和胶黏剂行业的可持续发展提供新的思路。
英文摘要:
      The work aims to use waste PET degradation products after pretreatment as chain extender to prepare adhesives with no formaldehyde release, strong adhesion, good durability and certain mechanical properties to replace traditional formaldehyde-based adhesives. A new type of polyurethane adhesive (PUa) was synthesized by elution of oligomer polyol prepared by high efficiency degradation of waste PET, and then step polymerization reaction with isocyanate. At low temperature/room temperature, PUa had bonding properties, and the adhesion strength to paper, glass, wood and other substrates exceeded 126 kPa. After 38 cycles of adhesion-deadhesion-adhesion, it still retained at least 39.2% adhesion, and had excellent repeatable bonding properties. The new polyurethane adhesive made from waste PET has good thermal stability and bonding properties, good environmental adaptability, and has great potential application value in the field of lightweight buffer packaging. The research can provide high value-added solutions for the resource utilization of plastic waste, and can also provide new ideas for alleviating the shortage of oil resources and the sustainable development of the adhesive industry.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第22546446位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号