覃宇奔,郑云磊,胡华宇,张燕娟,蒋婷,黄祖强.造纸污泥 / PVC 木塑复合材料的制备工艺[J].包装工程,2014,35(3):10-15,27.
QIN Yu-ben,ZHENG Yun-lei,HU Hua-yu,ZHANG Yan-juan,JIANG Ting,HUANG Zu-qiang.Preparation Technology of Paper Mill Sludge / PVC Wood Plastic Composites[J].Packaging Engineering,2014,35(3):10-15,27.
造纸污泥 / PVC 木塑复合材料的制备工艺
Preparation Technology of Paper Mill Sludge / PVC Wood Plastic Composites
投稿时间:2013-10-04  修订日期:2014-01-01
DOI:
中文关键词: 造纸污泥  木塑复合材料  偶联改性
英文关键词: paper mill sludge  wood plastic composite  coupling modification
基金项目:广西自然科学基金重点项目(2013GXNSFDA019004) ;广西大学科研基金资助项目( XJZ110619)
作者单位
覃宇奔 广西大学, 南宁 530004 
郑云磊 广西大学, 南宁 530004 
胡华宇 广西大学, 南宁 530004 
张燕娟 广西化工研究院, 南宁 530001 
蒋婷 广西大学, 南宁 530004 
黄祖强 广西大学, 南宁 530004 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究造纸污泥 / PVC 木塑复合材料的制备工艺。 方法 以造纸污泥为原料,PVC 为塑料基体,采用热压成形技术制备木塑复合材料,探讨污泥填充量、热压时间、温度、压力和偶联剂用量等因素对复合材料力学性能的影响,并采用扫描电镜和红外光谱对复合材料和造纸污泥进行表征。 结果 造纸污泥填充量为 50% ,偶联剂占污泥用量的 2% ,热压时间为 10 min,热压温度为 180 ℃ ,热压压力为 6 MPa 时,所制备复合材料弯曲强度为 35 . 73 MPa,拉伸强度为 12 . 75 MPa,具有良好的力学性能。 扫描电镜显示,经硅烷偶联剂改性后污泥与 PVC 制备的复合材料,界面相容性明显改善,材料力学性能明显提高。 红外光谱分析证明,偶联剂与造纸污泥发生了交联反应,形成了化学键接。 结论 采用造纸污泥与 PVC 共混制备木塑复合材料的工艺是可行的。
英文摘要:
      Objective To study the preparation technology of paper mill sludge / polyvinyl chloride ( PVC) wood plastic composites ( WPC) . Methods The WPC were prepared by hot press molding technology with paper mill sludge as reinforced material and PVC as plastics matrix, and the effects of paper mill sludge content, hot pressing time, temperature, pressure, and dosage of coupling agent on the mechanical properties of the composites were investigated, respectively. In addition, the composites and paper mill sludge were characterized by scanning electron microscope ( SEM) and Fourier transform infrared spectroscopy ( FT-IR) , respectively. Results Under the conditions of a paper mill sludge content of 50% , a weight percent of coupling agent / paper mill sludge of 2% , a hot pressing time of 10 min, a temperature of 180 ℃ , and a pressure of 6 MPa, the bending strength and tensile strength of the paper mill sludge / PVC composite were 35. 73 MPa and 12. 75 MPa, respectively, indicating the favorable mechanical properties of the composite. SEM analysis showed that the interfacial compatibility of the composite prepared by silane coupling agent-modified paper mill sludge and PVC was significantly improved, resulting in the enhancement of its mechanical properties. FT- IR analysis indicated that crosslinking reaction had occurred between the coupling agent and the paper mill sludge, forming chemical bonding. Conclusion It is feasible to prepare WPC with the blend of paper mill sludge and PVC.
查看全文   查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第20789322位访问者    渝ICP备15012534号-2

版权所有:《包装工程》编辑部 2014 All Rights Reserved

邮编:400039 电话:023-68795652 Email: designartj@126.com

    

渝公网安备 50010702501716号